HDPE Geomembrane Liner 0.5mm 0.75mm 1.0mm 1.5mm 2.0mm
Features:
- Excellent chemical resistance.
- Outstanding stress crack capacity.
- Lowest permeability.
- Excellent UV resistance.
- Stable low temperature embrittlement resistance.
- Complete width and thickness specifications.
- Cost effective.
- Proven performance.
- Fast deployment.
- Easy transportation.
- Meet or exceed all aspects of GRI GM13.
Description:
Introduction:
High density polyethylene(HDPE) smooth geomembrane, made of virgin resin by special production, has even and smooth surface on both sides. It is especially designed for flexible geomembrane.
Specification:
Thickness ranges from 0.2mm to 2.0mm, width from 1m to 8m. The roll length can be made according to design or customer request.
Property:
HDPE smooth geomembrane has excellent chemical and mechanical property, anti-crack property, dimensional stability and anti-aging property, furthermore it can be exposed for anti-UV property.
Application:
Municipal environmental, anti seepage in landscaping and municipal, metallurgy area, anti-corrosion, transportation infrastructure, agriculture reservoir waterproofing project, fisheries aquaculture. Other facilities waterproofing, anti erosion, anti seepage, reinforcement and seepage water collecting, preparation of temporary tank and special structure.
Technical Parameter :
| Spec Properties |
Test method ASTM |
GMS0.5 | GMS0.75 | GMS1.0 | GMS1.25 | GMS1.5 | GMS2.0 | GMS2.5 |
| Thickness | D5199 | 0.5mm | 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm |
| Density (≥ g/cc) | D1505 | 0.940 | 0.940 | 0.940 | 0.940 | 0.940 | 0.940 | 0.940 |
| Tensile Properties (Each direction) (≥) • yield strength • break strength • yield elongation • break elongation |
D 6693 Type IV |
8 kN/m 14kN/m 12% 700% |
11 kN/m 20kN/m 12% 700% |
15 kN/m 27 kN/m 12% 700% |
18 kN/m 33 kN/m 12% 700% |
22 kN/m 40 kN/m 12% 700% |
29 kN/m 53 kN/m 12% 700% |
37kN/m 67kN/m 12% 700% |
| Tear Resistance (≥) | D 1004 | 64 N | 93 N | 125 N | 156 N | 187 N | 249 N | 311 N |
| Puncture Resistance (≥) | D 4833 | 160 N | 240 N | 320 N | 400 N | 480 N | 640 N | 800 N |
| Stress Crack Resistance (≥) | D 5397 | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. |
| Carbon Black Content | D 1603 | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% |
| Carbon Black Dispersion | D 5596 | Note(1) | Note(1) | Note(1) | Note(1) | Note(1) | Note(1) | Note(1) |
| Oxidative Induction Time (OIT) (≥) (a)Standard OIT - or - (b)High Pressure OIT |
D 3895 D 5885 |
100 min. 400 min. |
100 min. 400 min. |
100 min. 400 min. |
100 min. 400 min. |
100 min. 400 min. |
100 min. 400 min. |
100 min. 400 min. |
Professional geosynthetics manufacturer
Anhui Zhonglu Engineer Materials Co., Ltd
Angela:86-18095658976
Email:angela@zhongloo.com